JX-705 Polyester single sided adhesive waterproof membrane

400-180-9696
Product Details

Overview

JX-705 PET self-adhesive waterproofing membrane is made of rubber modified asphalt self-adhesive material containing active additives as the main material, with polyester film (PET) as the surface reinforcement material on the upper surface and isolation film (paper) on the lower surface. It can be constructed by self-adhesive method (dry laying method) or cement adhesive (wet laying method), and can also be combined with rubber asphalt waterproof coating to form a composite waterproofing system. It is a tireless self-adhesive polymer modified asphalt waterproofing membrane that can meet the construction requirements of different base conditions.

圖片1.png

Features

l Strong bonding force, good extensibility of the self-adhesive layer, and strong ability to adapt to structural deformation.

l The overlapping seams of the roll materials are glued, and the overlapping and airtight performance is more reliable.

l The coil is soft and conformable, and has good construction tolerance.

l The fine cracks caused by nail rod penetration or external stress can heal themselves under the action of building load gravity.

l It has high reflectivity to sunlight, and short-term exposure can avoid UV and heat aging of the coil.

Specification

Width(m)

Thickness (mm)

Length (m)

Area (m2/roll)

1m

1.2mm, 1.5mm, 2mm

optional

15m, 20m

optional

15m2, 20m2

optional

Performance Index

China's implementation standard: GB 23441-2009 "Self-adhesive polymer modified bitumen waterproofing membrane" N-type PET membrane

No.

Test items

Technical indicators

Type I

Type II

1

Tensile properties

Pull   

≥150 N/50mm

≥200 N/50mm

Elongation at

maximum tension

30%

30%

Asphalt breaking elongation

≥150%

≥150%

2

Nail shank tear strength

≥30N

≥40N

3

Heat resistance

7 0℃ sliding no more than 2mm

4

Low temperature flexibility

-2 0

- 30

No cracks

5

Oil permeability                 

2

6

Stickiness

20 min

7

Waterproofness (0.2 MPa , 120min)

impermeable

8

Peel strength

Coil and Coil           

1.0 N/mm

Coil and sheet

1.5 N/mm

9

Water tightness of nail rod

pass

China's implementation standard GB/T35467-2017 "Wet-laid waterproofing membrane" Class H

No.

Test items

Technical indicators

1

Pull

≥300 N/50mm

2

Elongation at maximum tension

≥50%

3

Tear force

≥20N

4

Heat resistance (70℃, 2h)

No flow, dripping, slippage ≤ 2mm

5

Low temperature flexibility (-20℃)

No cracks

6

Waterproofness (0.3MPa, 120min)

impermeable

7

Coil to coil peel strength (lap edge)

No treatment

1N/mm

8

Oil permeability

≤2

9

Stickiness

≥30 min

Installation

Self-adhesive method.

2.png

Application

It is suitable for underground waterproofing projects and non-exposed roof waterproofing projects


Notes

1. Before the roll material is installed, avoid exposure to the sun to prevent the temperature from being too high and the isolation film from being difficult to tear open.

2. The joints of the roll materials should be dense.

3. Operations should be stopped in severe or extreme weather such as strong winds of level 5 or above, rain, snow, etc.

4. Before constructing the waterproof layer, the embedded parts must be installed and fixed to avoid drilling holes after the waterproof layer is constructed,

which will damage the waterproof layer and leave hidden dangers of leakage.

5. After the roll material is laid, areas that are directly exposed to sunlight for more than three weeks should be covered and protected with plastic sheets or other materials.